Ceronics Inc. is a manufacturer of metallic coatings that are fired on ceramic bodies. Our products range from molybdenum, tungsten and silver for electronics, to gold for decorative applications.

Since 1959, Ceronics, Inc. has been supplying a worldwide clientele who demand custom pastes that fit their unique application and firing guidelines. We can supply you with any size batch to meet your job requirements. Ceronics, Inc. can also make into paste form various types of metallic powder that is supplied to us.

We are manufacturers of ...

Molybdenum-Manganese Conductor Paste

Our Moly/Mang metalizing compositions are screen printable, thick film conductor paste used as a surface conductor on aluminum nitride, silicon nitride, beryllium oxide, and alumina substrate material.  These compositions are typically fired at high temperature in a reducing atmosphere.

   TECHNICAL PROPERTIES
  • Metalizing particle size less than 2 microns
  • Screened deposition thickness as fired approximately .0005 thick
  • Viscosity - Customized to meet your criteria
  • Shelf life of six months minimum
   TYPICAL DRYING CYCLE
  1. One hour ambient temperature  
  2. Thirty minutes at 150° F
  3. Thirty minutes at 450° F
  4. Parts should be kept hot until placed in metalizing furnace
  5. Cycle times can be reduced if drying lamps or other similar semi-automated cycles are used.
    TYPICAL FIRING CYCLE
  1. Atmosphere:  H Wet (75° Dew Point)
  2.  Temperature:  1300°C to 1580°C (depending on formulation)
  3. Time:  Thirty to forty five minutes at temperature
  4. Slow preheat and cool recommended.

M-20 Tungsten Conductor Paste

Our Tungsten metalizing compositions are screen printable, thick film conductor paste used for buried electrode layers in multiplayer ceramics.  These compositions are typically fired at high temperature in a reducing atmosphere after application to green ceramic tape.

   TECHNICAL PROPERTIES
  • Metalizing particle size less than 2 microns
  • Screened deposition thickness as fired approximately .0005 thick
  • Viscosity - Customized to meet your criteria
  • Shelf life of six months minimum
   TYPICAL DRYING CYCLE
  1. One hour ambient temperature  
  2. Thirty minutes at 150° F
  3. Thirty minutes at 450° F
  4. Parts should be kept hot until placed in metalizing furnace
  5. Cycle times can be reduced if drying lamps or other similar semi-automated cycles are used.
    TYPICAL FIRING CYCLE
  1. Atmosphere:  H Wet (75° Dew Point)
  2.  Temperature:  1300°C to 1700°C (depending on formulation)
  3. Time:  Thirty to forty five minutes at temperature
  4. Slow preheat and cool recommended.

24-Karat Burnishing Gold

Gold for china & porcelain decorating is also available. These products are available in various gold percentages.

Pictured is Ceronics gold on fine china custom decorated by our customer, Daisy Muff of Overland Park, Kansas.
  

Ceronics, Inc. also manufactures Nickel, Nickelous Oxide, Silver, and Silver/Palladium products to meet your specifications. We manufacture these products at high temperatures by metalizing compositions for screening, brushing, dipping and spraying.

Specializing in custom mixes to meet YOUR specifications.
  